Carbon Fiber Product Surface-Solution

 

 

High Gloss Varnish for Carbon Fiber Products

1. Product Features

 

This product is a special varnish that can be used for carbon fiber parts.

 

The VOC content of this varnish is less than 420gr/l. It is made of the latest raw materials on the market and is a state-of-the-art product that can be used for full overall painting and also for parts painting.

 

This product dries very quickly, has a good paint surface brightness, is particularly easy to polish, is not easy to scratch, and is UV resistant.

 

1. Application Range

l This new carbon fiber varnish can be applied to the surface of carbon materials, and can be sprayed on carbon material parts or entire vehicles.

 

3. Product Information
4. Color: transparent
5. VOC: <420g/L
6. Sprayable
7. Viscosity: Spraying viscosity 17-19 sec 4mm/DIN
8. Density: about 1.00g/cm3
9. Application period (gel time): 2 hours with curing agent at 20℃
10. Shelf life: 1 year
11. Flash point: 23℃9. Dry film bonding strength: 50-70 microns

 

4. Usage

Surface sprayed with gel coat or carbon fiber spray putty

 

5. Mixing Ratio

 

By volume: 2:1By weight: 100g(A):50g(B)

 

It is recommended to use the whole set of carbon fiber products together.

If mixed with other non-carbon fiber products, there may be problems in drying time and adhesion.

 

1. Application:
2. Spraying: Spraying can be done gradually, and each coating should not be too thick
3. Spraying: Spray until the coating surface flows evenly. Wait for 5-10 minutes (interval) after each spraying to allow the surface material to evaporate

 

VII. Drying Time

1. When the baking temperature is 70℃, it takes about 45 minutes,
2. When the natural temperature is 20℃, it takes about 12 hours. The hardness test needs to reach 48H.

VIII. Polishing

 

After drying in the oven, it should be cooled first and then polished. 2004/42/IIB (d) (420) < 420:

This product (belonging to 11B.d) has a maximum EU standard of no more than 420g/l

This product has a VOC content of less than 420g/l

 

Carbon Fiber Matte Varnish

1. Product Features

This product is a special varnish that can be used for carbon fiber parts. This varnish has a VOC content of less than 420gr/l and is made of the latest raw materials on the market. It is a state-of-the-art product that can be used for full overall painting and component painting. This product dries very quickly, has a bright paint surface, is particularly easy to polish, is not easy to scratch, and is UV resistant.

 

2. Application Scope

This new carbon fiber varnish can be applied to the surface of carbon materials, and can be sprayed on carbon fiber parts or entire vehicles.

 

3. Product Information

 

1. Color: transparent
2. VOC: <420g/L
3. Sprayable
4. Viscosity: Spraying viscosity 17-19sec4mm/DIN
5. Density: about 1.00g/cm3
6. Applicable period (gel time): 2 hours with curing agent at 20℃
7. Shelf life: 1 year
8. Flash point: 23℃
9. Dry film bonding strength: 30-50 microns
10. Glossiness: 8-15 degrees under 90-degree irradiation of gloss meter.

 

4. Usage

Surface has been sprayed with gel coat or carbon fiber spray putty

 

5. Mixing Ratio

By volume: 2:1By weight: 100g (A): 50g (B)

It is recommended to use the whole set of carbon fiber products together.

If mixed with other non-carbon fiber products, there may be problems in drying time and adhesion.

 

6. Application: Spraying: It can be sprayed gradually, and the coating should not be too thick each time. Spraying: Spray until the coating surface flows evenly. Wait for 5-10 minutes (interval) after each spraying to allow the surface material to evaporate.

 

7. Drying Time
8. When the baking temperature is 70℃, it is about 45 minutes,
9. When the natural temperature is 20℃, it is about 12 hours. The hardness test needs to reach 48H.

 

Note:

2004/42/IIB(d)(420)<420:

The EU standard for this product (belonging to 11B.d) is no more than 420g/l

This product VOC content is less than 420g/l

 

Carbon Fiber Nano Crystal Coating (Transparent Spray Putty)

 

1. Product Features
2. Good filling performance
3. Smooth ductility, easy to paint
4. Easy to fill and non-porous
5. Easy to grind or sandblast
6. High transparency
7. Anti-ultraviolet, no yellowing

 

1. Product Information
2. Product viscosity at 20℃: paste
3. Volatile organic compound content: 2004/42/IIB(b)(250)<250g/l
4. Color: transparent

 

III. Substrate Surface

The substrate surface must be clean, dry and free of oil. The substrate must be grinded or sandblasted before spraying

 

1. Operation Mixing Ratio
2. Scraping method: Use 1.0% to 1.5% of the main agent weight of curing agent.
3. Spraying method: Add 10% to 20% of diluent on the basis of the above.

The paint/curing agent/thinner must be fully mixed.

 

1. Application Period (Gel Time)

Room temperature 20℃, 60 minutes

 

1. Reaction Temperature

Minimum 5℃ or above.

 

VII. Application:

The application scope of this product includes carbon fiber products and composite materials products sprayed with 1.8-2.0MM caliber spray gun.

 

VIII. Drying Time

Room temperature 25℃ environment, 2-3 hours baking 70℃@30 minutes

 

1. Storage Conditions

25℃ sealed original packaging, about 12 months. Store in a cool, ventilated environment, avoid direct sunlight, away from chemically incompatible items and fire sources. No unauthorized movement.